Osaka Gas Chemicals Release New Special Silicone Coating Featuring Outstanding Non-Stick Properties, Excellent Hardness and Low Processing Temperature

2018年09月11日 PM10:00
このエントリーをはてなブックマークに追加


 

OSAKA, Japan

Osaka Gas Chemicals has developed Silicera Coat 8011, a special silicone coating that offers outstanding non-stick properties and hardness far exceeding that of fluoropolymer coatings. Silicera Coat 8011 will provide new solutions to the problems of mold releasing and sliding of industrial mechanical components (such as rollers and guides) that cannot be solved with existing fluoropolymer coatings.

Features of Silicera Coat 8011

  • Excellent non-stick properties showing promising applications in food processing facilities (also offering non-stick durability, achieving higher performance as compared with fluoropolymer coatings)
  • Treated at lower temperatures (100°C – 250°C), reducing the risk of heat deformation
  • Achieved higher pencil hardness (9H) outperforming fluoropolymer coatings (with typical hardness of H)
  • Good sliding properties suitable for coating on transfer system components
  • Coating material compliant with the Food Sanitation Act, Japan and the U.S. FDA guidelines, permitted for use in food applications
 

Properties of Silicera Coat 8011

Pencil
hardness

 

Tape peel
load*1

 

Contact
angle with
water

  Sliding  

Coating
thickness

 

Treatment
temperature

 

Heat
resistance*2

9H   0 g   100  

Good

  30 μm -
50 μm
 

100°C -
250°C

  300°C
*1:   Measured tape peel load using a surface properties measuring instrument.
*2: Non-stick properties will decline at an ambient temperature over 200°C although the material is heat resistant up to 300°C.
 

Examples of applications

  • Heat sealing plates (mold releasing, heat resistance)
  • Guides and covers (prevention of adhesion)
  • CFRP rollers (non-stick)
  • Rollers (non-stick, wear resistance)

* Color of Silicera Coat 8011 is metallic black.

 
Silicera Coat 8011 coating specifications
[1] 8011BK-AS (base coat A)             3 kg
[2] 8011TM-AS (top coat A) 3 kg
[3] 8011BS (solution B, common) 2 kg
 
  • Mix base coat A and base coat B with solution B at the specified ratio, respectively.
  • Spray Silicera Coat (wet on wet) onto a substrate and place it in a drying furnace for a baking finish (at 100°C to 250°C).
    * Shot-blast the substrates to be coated as a pretreatment.

For details of Silicera Coat, visit the Osaka Gas Chemicals website:
http://business.atengineer.com/ogc-en/

View source version on businesswire.com: https://www.businesswire.com/news/home/20180911005026/en/

CONTACT

Osaka Gas Chemicals
Tadaaki Kotani, +81-6-4804-8380
siliceracoat@ml.ogc.co.jp

Related Posts Plugin for WordPress, Blogger...

同じカテゴリーの記事 

  • Takeda to Divest TachoSil® to Corza Health for €350 Million
  • 新たな研究:ハンドドライヤーによる手の乾燥はペーパータオルと同じくらい衛生的
  • Body Fit Training PTY LTD Sues to Invalidate F45 Training PTY LTD’s U.S. Patents
  • Singapore and Apple Partner on National Health Initiative Using Apple Watch
  • 最新研究:干手机与用纸巾擦干双手一样卫生